Powder spheroidization methods include physical methods and chemical methods.

According to different material aggregation modes, the preparation methods of spherical alumina can be systematically classified into three categories: gas-phase method, liquid-phase method, and solid-phase method.

As one of the commonly used adsorbents, the adsorption effect of alumina balls is obvious. If the adsorption effect is not ideal during use, it is necessary to check which factors have affected the adsorption performance of the product. Generally, the main factors affecting the adsorption effect of alumina balls are as follows:

Methods of Alumina Powder Spheroidization

Powder spheroidization methods include physical methods and chemical methods. According to different material aggregation modes, the methods for preparing spherical alumina can be systematically classified into three categories: gas-phase method, liquid-phase method and solid-phase method.

1. Ball Milling Method

The ball milling method is the most common technique for preparing ultrafine alumina powder. Usually, relying on the rotation or vibration of a ball mill, raw materials are impacted, ground and stirred by abrasives, and large-particle-size powder is refined into ultrafine powder. The particle size of the prepared spherical alumina powder mainly depends on the particle state of the raw materials and the preparation process.

Advantages: Simple operation, low cost and high output.

Disadvantages: The surface of the prepared spherical powder particles is relatively rough, resulting in increased specific surface area and enhanced powder activity, which easily causes inter-particle agglomeration. Thus, it is not suitable for preparing spherical powder particles with high-quality requirements.

2. Homogeneous Precipitation Method

The precipitation process in a homogeneous solution involves nucleation, followed by aggregation and growth, and finally precipitation from the solution, which is usually in a non-equilibrium state. However, if the concentration of the precipitant in the homogeneous solution can be reduced or even generated slowly, a large number of tiny nuclei will be uniformly formed. The resulting fine precipitate particles will be uniformly dispersed in the entire solution and maintain an equilibrium state for a relatively long time. This method of obtaining precipitation is called the homogeneous precipitation method. For the homogeneous precipitation method, if the size of the obtained precipitate particles is within the range of colloidal particles, this method is also known as the sol-gel method.

Advantages: Mild reaction conditions, high sphericity, average particle size of 400nm～10μm, low purity and good dispersibility.

Disadvantages: To obtain spherical powder, aluminum sulfate must usually be used as the raw material, so harmful sulfides are generated during the calcination stage. Agglomeration and porous channels occur after sintering.

3. Sol-Gel Method

The sol-gel method uses alkoxides or inorganic salts to form precursor sol through hydrolysis or polymerization reactions, followed by alcohol washing, aging and finally calcination to obtain alumina powder. The pH value of the system and the concentration of reactants must be precisely controlled when using this method.

Advantages: Good uniformity and high chemical purity.

Disadvantages: The preparation process is relatively complex and the cost is high.

4. Sol-Emulsion-Gel Method

This method is developed on the basis of the sol-gel method. In the early stage, the sol-gel method was mostly used to prepare alumina sol, and more research focused on the microstructure of the obtained colloid. Gradually, this method became a common technique for preparing ultrafine powder. To obtain spherical powder particles, the interfacial tension between the oil phase and the water phase is used to form tiny spherical droplets, so that the formation and gelation of sol particles are confined within the tiny droplets, and finally spherical precipitate particles are obtained. In the sol-emulsion-gel method, a large amount of organic solvents and surfactants are used to form the emulsion. The separation process of spherical powder in the emulsion is very cumbersome, and it is not easy to maintain the spherical shape of the powder during the drying and calcination stages.

5. Dropping Ball Method

The dropping ball method is a technique in which alumina sol is dropped into an oil layer (usually paraffin, mineral oil, etc.). Spherical sol particles are formed by the action of surface tension, then the sol particles are gelled in ammonia solution, and finally the gel particles are dried and calcined to form spherical alumina. This method is a further improvement on the sol-emulsion-gel method in terms of process. It applies emulsion technology to the aging stage of the sol, keeps the oil phase stationary, and eliminates the separation process between the powder and the oily reagent.

1. Used as ceramic materials Spherical micropowders exhibit excellent press-forming and sintering properties, which are extremely beneficial for producing high-quality ceramic products.

Part of alumina balls are suitable for ultra-fine grinding. Whether they can meet the requirements mainly depends on their purity, particle size, specific grinding materials and target fineness.

1.Used as Ceramic Material 

Spherical micro-powder exhibits excellent press-forming and sintering properties, which are highly beneficial for producing high-quality ceramic products.